JCC film adhesives are produced with or without release paper,, which can be conveniently operated by continuous or intermittent process. Based on the experiences and advantages in hot melt adhesive raw material, JCC developed a full range of film adhesive by different processes: spraying, casting, coating, blowing to meet the requirement of different applications.
|
Type
|
Feature
|
Applicable Material
|
| PES Adhesive Film | Excellent washing resistance. | Metal, ceramic, fabric, wood, plastic |
| PA Adhesive Film | Good resistance to heat, cold, oil, chemical, mediums. No smell, no spot, fast curing | Leather, fabric, plastic, metal |
| TPU Adhesive Film | Good flexibility and mechanical properties, suitable for high speed automatic production, safe and environmentally friendly | Leather, fabric, plastic, metal, Glass |
| EVA Adhesive Film | Outstanding adhesion, softness, heat mobility, cold resistance | EVA has large cohesion force and low surface tension, thus has thermal adhesion to almost all substrates. |
| PO Adhesive Film | odorless, non-toxic, good resistance to cold and chemicals | Mainly used for packaging paper, carpet, aluminium-plastic panel |
Applications
●Reflective Material
●Laser Firing
●Labels
●Shoes Material
●Conductive Fabric
Technical Data
|
Type
|
PA
|
PES
|
EVA
|
PO
|
TPU
|
|||||||||||
| Item No. | F801 |
F908 |
F918 | F907 | F917 | F9201 | F9203 | F901 | F901T | F505 | F506 | F701 | F601 | F603 | F6202 | F6201 |
| Release | Release Paper | No Release | PE Transparent Film | PE Release Film | Release Paper | No Release | No Release | Release Paper | PE Release Film | PE Release Film | ||||||
| Melting Point | 98-115 | 90-110 | 90-125 | 90-125 | 95--130 | 85-105 | 65-80 | 115-130 | 110-120 | 115-130 | 120-130 | 110-120 | ||||
| Press temperature | 140 | 150 | 150 | 150 | 150 | 130 | 130 | 140 | 140 | 150 | 150 | 140 | ||||
| Washing Resistance | 优 | 优 | 优 | 优 | 优 | 一般 | 一般 | 好 | 好 | 好 | 好 | 好 | ||||
| Thickness | 5-20 | 4-10 | 4-10 | 4-10 | 5-20 | 2.5-10 | 10-20 | 5-20 | 5-20 | 5-20 | 4-10 | 4-10 | ||||